產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.12 | % | |
| 物理性能 | 阻燃性 | 2.5mm | UL 94 | V-0/5VA | ||
| 阻燃性 | 0.75mm | UL 94 | V-0 | |||
| 阻燃性 | 0.43mm | UL 94 | V-2 | |||
| 比重 | JIS K-7112 | 1.46 | ||||
| 機械性能 | 拉伸強度 | ASTM D-638 | 118(1200) | Mpa(kgf/cm2) | ||
| 斷裂伸長率 | ASTM D-638 | 2.5 | % | |||
| 彎曲模量 | ASTM D-790 | 7410(75500) | Mpa(kgf/cm2) | |||
| 彎曲強度 | ASTM D-790 | 157(1600) | Mpa(kgf/cm2) | |||
| 耐沖擊強度值 | 艾氏、帶缺口厚度3.2mm | ASTM D-256 | 98(10) | J/m(kgf·cm/cm) | ||
| 壓縮強度 | ASTM D-695 | 143(1460) | Mpa(kgf/cm2) | |||
| 拉伸模量 | ASTM D-638 | 8240(84000) | Mpa(kgf/cm2) | |||
| 洛氏硬度 | ASTM D-785 | 93 | M標度 | |||
| 耐沖擊強度值 | 艾氏、帶缺口厚度6.4mm | ASTM D-256 | 98(10) | J/m(kgf·cm/cm) | ||
| 電氣性能 | 介電正切 | 106Hz | ASTM D-150 | 0.009 | ||
| 介電率 | 60Hz | ASTM D-150 | 3.51 | |||
| 介電正切 | 60Hz | ASTM D-150 | 0.0009 | |||
| 耐導電徑跡性（CTI） | IEC 112 | 180 | V | |||
| 絕緣破壞強度 | 快速加壓值厚度1.6mm | ASTM D-149 | 30 | kv/mm | ||
| 體積電阻率 | ASTM D-257 | 1×1016 | Ω.cm | |||
| 耐電弧性 | ASTM D-495 | 100 | sec | |||
| 介電率 | 106Hz | ASTM D-150 | 3.41 | |||
| 加工性能 | 成型收縮率 | 流動方向 | ASTM D-955 | 0.02～0.2 | % | |
| 垂直方向 | ASTM D-955 | 0.3～0.5 | % | |||
| 熱性能 | 負荷撓曲溫度 | 負荷1.813MPa(18.6kgf/cm2) | JIS K-7207 | 149 | ℃ | |
| 線膨脹系數(shù) | 流動方向 | ASTM D-696 | 2.0 | 10-5cm/cm/℃ | ||
| 垂直方向 | ASTM D-696 | 5.6 | 10-5cm/cm/℃ | |||
| 溫度指數(shù) | 電學式 | 厚度1.47mm | UL 746B | 130 | °C | |
| 沖擊式 | 厚度1.47mm | UL 746B | 120 | °C | ||
| 非沖擊式 | 厚度1.47mm | UL 746B | 130 | °C | ||
| 負荷撓曲溫度 | 負荷0.451MPa(4.6kgf/cm2) | JIS K-7207 | 151 | ℃ | ||