TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
540
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
430
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
5
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
50
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
22400
|
kgf/cm2
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
810
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
22400
|
kgf/cm2
|
ASTM D 790
|
|
Tensile Stress, yield, 50 mm/min
|
50
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
40
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
4
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
>40
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2100
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
75
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2100
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C
|
81
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
11
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
509
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, notched 80*10*4 +23°C
|
50
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 0°C
|
15
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
10
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
52
|
kJ/m2
|
ISO 179/1eA
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
105
|
°C
|
ASTM D 1525
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
75
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
8.84E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
8.97E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, flow
|
8.84E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
8.97E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate B/50
|
122
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
123
|
°C
|
ISO 306
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
77
|
°C
|
ISO 75/Af
|
|
Relative Temp Index, Elec
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
120
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.3
|
-
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.7 - 1
|
%
|
SABIC Method
|
|
Melt Flow Rate, 266°C/5.0 kgf
|
35
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.3
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.1
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.03
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 265°C/2.16 kg
|
11
|
cm3/10 min
|
ISO 1133
|
|
Melt Viscosity, 260°C, 1500 sec-1
|
260
|
Pa-s
|
ISO 11443
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
UL Compliant, 94V-0 Flame Class Rating (3)(4)
|
1.5
|
mm
|
UL 94 by SABIC-IP
|
|
UL Compliant, 94-5VA Rating (3)(4)
|
3
|
mm
|
UL 94 by SABIC-IP
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.5
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3)
|
3
|
mm
|
UL 94
|
|
Glow Wire Flammability Index 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Flammability Index 960°C, passes at, by VDE
|
3
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Ignitability Temperature, 1.0 mm
|
825
|
°C
|
IEC 60695-2-13
|
|
Glow Wire Ignitability Temperature, 3.0 mm
|
725
|
°C
|
IEC 60695-2-13
|
|
UV-light, water exposure/immersion
|
F1
|
-
|
UL 746C
|