| NORYL GTX? Resin | ||
| Grades |
De |
|
| GTX4610 |
PPE+PA, Glass, Datasheet Product Data: Auto Data: |
|
| GTX673 |
PPE+PA, Conductive, Datasheet Product Data: Auto Data: |
|
| GTX678 |
PPE+PA, Flame Retardant, Conductive, Heat Stabilized, Impact Modified, Nonhalogenated, Datasheet Product Data: Auto Data: |
|
| GTX8730 |
PPE+PA, Glass, Conductive, Datasheet Product Data: Auto Data: |
|
| GTX902D |
NORYL GTX902D is a GTX902E with smaller shaped pellets. Datasheet Product Data: Auto Data: |
|
| GTX975 |
18% mineral filled conductive NORYL GTX. Datasheet Product Data: Auto Data: |
|
| GTX989 |
PPE+PA, Conductive, High Impact, Datasheet Product Data: Auto Data: Auto Specification |
|
| NX0031 |
PPE+PA, conductive with high impact Datasheet Product Data: Auto Data: |
|
NORYL GTX ? Resin GTX975 |
SI | | British | | Metric | Americas: COMMERCIAL |
| NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting in an unique way. |
|
Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 700 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 690 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3.5 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 4.5 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 45300 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1150 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 40700 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 65 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 65 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3.5 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 4 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4200 | MPa | ISO 527 | |
| Flexural Stress, break, 2 mm/min | 110 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 4000 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 3 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 3 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 30 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m2 | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m2 | ISO 179/1eU | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 210 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 5.4E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ASTM E 831 | |
| CTE, 23°C to 60°C, flow | 5.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 6.5E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 195 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 185 | °C | ISO 75/Be | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.25 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.8 - 1.2 | % | SABIC Method | |
| Melt Flow Rate, 280°C/5.0 kgf | 15 | g/10 min | ASTM D 1238 | |
| Density | 1.2 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 3.5 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 1.1 | % | ISO 62 | |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 10 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | 1.E+03 - 1.E+04 | Ohm-cm | SABIC Method | |
| Source GMD, last updated:2007/11/26 |
|
Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 100 - 110 | °C |
| Drying Time | 2 - 3 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 300 - 320 | °C |
| Nozzle Temperature | 280 - 300 | °C |
| Front - Zone 3 Temperature | 300 - 320 | °C |
| Middle - Zone 2 Temperature | 280 - 300 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Hopper Temperature | 80 - 100 | °C |
| Mold Temperature | 100 - 120 | °C |
| Source GMD, last updated:2007/11/26 |